aula de restaurações indiretas estéticas

Prévia do material em texto

1 
Restaurações 
Indiretas 
Não-Metálicas 
Prof. Dr. Adalberto B. de Vasconcellos 
FOUFF/NF 
ü  INLAYS 
ü  ONLAYS 
ü  OVERLAYS 
ü  COROAS TOTAIS 
ü  PRÓTESE PARCIAL FIXA 
RESTAURAÇÕES 
INDIRETAS ADESIVAS 
ESTÉTICAS 
VASCONCELLOS, A. B. 
CLASSIFICAÇÃO 
 
 Qto ao material odontológico 
VASCONCELLOS, A. B. 
 
 
ü  RESINA COMPOSTA 
ü  RESINA COMPOSTA DE 
LABORATÓRIO (CERÔMERO) 
ü  CERÂMICAS ODONTOLÓGICAS 
 
FOUFF/NF 
 INLAYS 
VASCONCELLOS, A. B. 
Qual o melhor material? 
 
FOUFF/NF 
COSTA et al., 2015 
RESINA COMPOSTA 
 
FOUFF/NF 
COSTA et al., 2015 
LIGA METÁLICA 
OURO 
2 
 
MODELO ELASTOMÉRICO 
 
VASCONCELLOS, A. B. 
INLAYS / PREPARO DENTÁRIO 
VASCONCELLOS, A. B. 
VASCONCELLOS, A. B. VASCONCELLOS, A. B. 
COMPÓSITOS DE 
ALTA DENSIDADE 
QUI X FIL (DENTSPLY) 
XENO III (DENTSPLY) 
VASCONCELLOS, A. B. VASCONCELLOS, A. B. 
3 
RESINAS 
COMPOSTAS DE 
 LABORATÓRIO 
VASCONCELLOS, A. B. 
ARTGLASS 
(KULZER) 
VASCONCELLOS, A. B. 
 
CERÔMERO 
 
TARGIS / VECTRIS 
(IVOCLAR) 
VASCONCELLOS, A. B. 
 
CERÔMERO 
 
VASCONCELLOS, A. B. 
 
CERÔMERO 
 
RESTAURAÇÕES INDIRETAS 
ADESIVAS ESTÉTICAS 
 CERÂMICAS 
ODONTOLÓGICAS 
Prof. Dr. Adalberto B. de Vasconcellos 
 
FOUFF / NF 
ü  FELDSPÁTICAS 
ü ALUMINIZADAS 
ü ALUMINIZADAS INFILTRADAS DE 
VIDRO 
ü VIDROS CERAMIZADOS 
VASCONCELLOS, A. B. 
COMPOSIÇÃO QUÍMICA 
 
CLASSIFICAÇÃO 
 
4 
ü FASE CRISTALINA : quartzo - forma 
cristalina da sílica ( SiO2 ) 
ü FASE VITROSA ( matriz ) : feldspato 
ü CAULIN : silicato de alumina hidratado 
VASCONCELLOS, A. B. 
 
FELDSPÁTICA 
 
VASCONCELLOS, A. B. 
 
FELDSPÁTICA 
 
CASO 
CLÍNICO 
ü McLean & Hughes, 1965 
ü FASE CRISTALINA : 50% de Al2O3 
ü FASE VITROSA ( matriz ) : feldspato 
VASCONCELLOS, A. B. 
 
ALUMINIZADA 
 
 
ALUMINIZADA 
 
VITADUR ALPHA / VITA 
VASCONCELLOS, A. B. 
➨  97% de Al2O3 
➨ Sadoun, 1985. 
 
ALUMINIZADA 
INFILTRADA DE VIDRO 
 
 
 VASCONCELLOS / FOUFF 
 
 VASCONCELLOS / FOUFF 
 
ALUMINIZADA 
INFILTRADA DE VIDRO 
 
5 
In-ceram alumina / VITA 
 
ALUMINIZADA 
INFILTRADA DE VIDRO 
 
 
 VASCONCELLOS / FOUFF 
 
 VASCONCELLOS / FOUFF 
ü  The crystal structure of zirconium 
dioxide is made stable at room 
temperature by an addition of 
yttrium oxide. 
ü  VITA YZ T can be used to fabricate 
delicate substructures for crown 
and bridge restorations with a high 
precision of fit. 
ü  VITA YZ HT is a highly translucent 
zirconia which is particularly 
suitable for monolithic restorations 
due to its enormous strength 
(approx. 1,200 MPa) and excellent 
light refraction properties. 
 
VIDRO CERAMIZADO 
 
 
 VASCONCELLOS / FOUFF 
 
CRISTALIZAÇÃO DIRIGIDA 
 
 
 VASCONCELLOS / FOUFF 
 
IPS EMPRESS (IVOCLAR) 
 
 
 VASCONCELLOS / FOUFF 
• MAQUIAGEM : EMPRESS - leucita 
• ESTRATIFICADA : EMPRESS 2 
(dissilicato de lítio) + cerâmica de 
revestimento (Eris) 
6 
 
IPS EMPRESS 2 (IVOCLAR) 
 
 
 VASCONCELLOS / FOUFF 
 
IPS EMPRESS 2 (IVOCLAR) 
 
 
 VASCONCELLOS / FOUFF 
 
IPS EMPRESS 2 (IVOCLAR) 
 
 
 VASCONCELLOS / FOUFF 
 
IPS e.max Press (IVOCLAR) 
 
 
 VASCONCELLOS / FOUFF 
•  Indications: single-tooth restorations, bridges for the 
anterior and premolar region, inlays, onlay, implant 
superstructures and custom implant abutments 
 
IPS e.max CAD (IVOCLAR) 
 
 
 VASCONCELLOS / FOUFF 
•  Indications: single-tooth restorations, bridges for the 
anterior and premolar region, inlays, onlay, implant 
superstructures and custom implant abutments 
 
IPS ZirCAD (IVOCLAR) 
 
•  Characteristics: is a yttrium-stabilized zirconium oxide 
blockhigh final flexural strength (>900 Mpa); the frameworks 
are conventionally veneered with the IPS e.max Ceram 
layering ceramic or pressed over with IPS e.max ZirPress. 
•  Indications: long-span posterior or anterior bridges 
7 